Filamento Fibra de Carbono + PLA - Carbon X Impressão 3D
Carbon fiber filament X ( Carbon fiber+PLA);Carbon fiber pla
High rigidity Black
Carbon fiber combined with PLA filament. The proportion of carbon fibers comprise 20% by weight,80% by volume.
Carbon fiber is of high rigidity and it is very fragile, not suitable for printing hollow,thin, single structure item which lower than 3mm.
Please better print solid item or multi-filling structure.
• Environment friendly and biodegradable • Product models
• Low shrinkage, excellent dimensional stability • Art crafts
• High stiffness and toughncss • Adornments
Recommended Printing Temperature (°C):200-220
Recommend Heatbed Temperature (°C): 100-120
Properties Test Standard Test Condition S.I Unit S.I Typical value ( Printing/Injection Moulding)
Density ISO 1183 23°C g/cm3 1.29
Glass transition Temperature ISO1 1357 1O°C/min °C 60
Melt lndex ISO 1133 190°C,2.16kg g/lOmin 4.5
Tensile strength ISO 527 50mm/min MPa 31.2
Elongation at break ISO 527 50mm/min % 6.3
Bending Strength ISO 178 2m/min MPa 40.2
Bending modulus ISO 178 2m/min MPa 2200
lzod lmpact, Notched ISO 180 23°C KJ/m² 5.5
Heat distortion temperature ISO75 0.45MPa °C 57
Flammability UL94 1.6mm Class HB
[I] These are typical values of the product's properties and these values alone do not represent a sufficicnt basis for any part
design and are not intended for use in establishing maximum. ,minimum. or ranges of values for specífication purposes.
 The listed values are maybe different for pigmented material.
Printing temperature = 210°C, printing speed =80mm/s, number of shells = 2, Nozzle size = 0.4mm, and 100% infill.
processing conditions: Temperature = 200°C, Back pressure: 0-1MPa: mould temperature: 30-40°C
Typical Conditions of Printing
Printing Recommendation Typical Range
Extruder Temperature 210-230°C
Printing Speed 30-100mm/s
Bed Temperature Room temperature - 50°C
Layer Height 0.1-0.2mm
lnfill As need up to 100%
Matters need attention General print
The parameter is just for referencial purpose only.
In actual processing, the parameter should adjusted by construction of 3D machine, shape and size of product, and so on.